HDPE Pipe Welding Machine Equipment Has Strong Thermal Storage Capacity And Timely Replenishment Capacity

2018-11-15

How to weld HDPE Pipe Welding Machine to ensure the quality of PP-R tubing welding:

One, must choose the quality qualified hot melt welder.

Shan temperature control should be correct. PP-R Hot Melt Welding temperature is: 253. If the temperature is below 253 Shan, the pipes and fittings are only a thin surface of the melting, once they are fused between, the strength of the weld is not guaranteed, this is what we usually call false welding phenomenon; Conversely, if the temperature is above 274 Shan, the surface molecules of pipes and fittings are destroyed by high temperature, so that pp-r form thin liquid, after connecting will make the pipe diameter smaller, more importantly, the connection part will occur brittle crack, especially in the piping system completed after the water pressure, Such problems often occur.

Shan constant temperature time is long. The length of the constant temperature is one of the important symbols of the performance of hot-melt welding equipment. Hot-melt equipment still has a heat consumption problem after heating up to set temperature, especially in the winter, the tuyere, even in the non operating gap, its heat consumption is also very large, and once the operation, its pipes and fittings are separately consumed heat energy, which requires the equipment has a strong thermal storage capacity and timely replenishment capacity.

Second, must choose the qualified and suitable welding sleeve.

योग्य वेल्डिंग आस्तीन को पूरी तरह से वेल्डिंग के बाद अनुप्रस्थ संरचना और पाइप की वेल्ड गहराई, साथ ही साथ सतह की चिपचिपाहट और सतह की चिकनाई पर विचार करने के लिए डिज़ाइन किया गया है। वर्तमान में, पीपी-आर, पीपीसी, पीई और अन्य पानी के पाइप निर्माताओं के गर्म पिघल वेल्डिंग विधि के घरेलू उत्पादन सैकड़ों हैं। क्योंकि कच्चे माल, एडिटिव्स, विभिन्न पर्यावरणीय परिस्थितियों, उपकरण चयन के उत्पादन के निर्माता, ताकि पाइप और पाइप के आकार का उत्पादन अलग-अलग हो। इसलिए, पाइप निर्माताओं और उपयोगकर्ताओं को अपने स्वयं के पाइप व्यास वेल्डिंग आस्तीन का चयन करना होगा। ऑपरेटर के लिए, वेल्डिंग भाग में अशुद्धियों से बचने के लिए वेल्डिंग आस्तीन की सतह को साफ करने के लिए अंतिम वेल्डिंग के बाद आवश्यक होना चाहिए।

40 मिमी से अधिक कैलिबर वाले पाइप के लिए, बड़े कैलिबर और गैर-व्यक्तिगत शक्ति की क्षमता के कारण, पाइप में गहराई और सीधे पाइप में प्रवेश सुनिश्चित करने के लिए यांत्रिक उपकरणों का उपयोग करना आवश्यक है। हमने पाया कि वेल्डिंग के लिए 110 मिमी इंटरफ़ेस पर पांच से छह श्रमिकों वाले कई निर्माण स्थलों में, शुल्क डिकेंस पाइप की सीधेपन और सम्मिलन की गहराई, पूरे पाइपलाइन घुमावदार की गारंटी नहीं दे सकता है, एक निश्चित तापमान और दबाव की स्थिति में कल्पना करना मुश्किल है।

तीसरा, समस्याओं को हल करने में आसान में गर्म पिघल वेल्डिंग।

It should be said that in strict accordance with the welding process and welding technology requirements of the construction operation of the pipeline system, under normal temperature and pressure to use is not a problem. However, we often find in the day-to-day construction of pipes and fittings in the junction of a burst phenomenon or sand.

The main reasons are as follows:

शान हॉट पिघल वेल्डर तापमान सही नहीं है, बहुत अधिक या बहुत कम है, पॉलीप्रोपाइलीन के प्रदर्शन को बदल दिया जाता है;

Shan the surface of the welding sleeve is not properly disposed, or the surface coating falls off to make the contact part of the pipe produce sand hole;

The size of the Shan welding sleeve is not correct, so the melting depth and weld structure of the pipe are not suitable.

The welding surface of the pipe is not cleaned before the Shan welding.

Shan welded pipes and fittings do not maintain concentric or straight lines.

IV. Correct welding operation procedure.

Preparation of Shan hot-melt welding

Shan for the outer diameter 25-110mm pipe to chamfer the beveling mouth to 15 chamfer to the original tube wall thickness of half;

The Shan is cleaned with a cleaning machine (or alcohol) and a brush to the surface of the weld part of the pipe;

Shan when a pre assembled part is fused, the connection is marked in the position required by the pipe and the fitting.

Sham 40mm caliber above the pipe welding must use the plane and the vertical pipe welding machine;

After each dissolution, Shan should use dry cloth or dry paper to clean the heating sleeve and heating head, do not use detergent.

Shan Hot Melt and connection

Shan The tubes and fittings are inserted into the heating sleeve and the heating head, do not rotate or move too fast (to make the material melt time).

After the Shan is heated, remove the pipes and fittings from the heating element and do not rotate the heating part.

Shan the pipe and fittings are pressed along the axis immediately after heating, do not rotate. Strictly adhere to the hot-melt welding standards to maintain the time and cooling time.